S55C steel

S 55 C steel plate,JISG4051 S 55 C steel plate, under JISG4051 standard, we can regard S 55 C steel plate as high carbon steel.

JIS G4051 S 55 C steel plate is one mainly of high carbon steel,is treated high technical heat treatment and it helps you make Die Plate & Plastics Die Plate much easier with good quality.It is equal to EN C55,DIN17200 C55,BS970 070M55,SAE 1055 and so on.

S55C steel equivalent standards

  S55C
JIS G 4051
Number:1.0535

Comparision of steel grades

EN 10083-2 C 55
DIN 17200 C 55
NFA 33-101 AF70-C 55
UNI 7846 C 55
BS 970 070 M 55
UNE 36011 C 55 k
SAE J 403-AISI 1055

S55C steel Chemical Composition

Grade C(%)min-max Si(%)min-max Mn(%)min-max P(%)max S(%)max Cr(%)min-max
S55C 0.52-0.60 0.15-0.35 0.60-0.90 0.025 0.025 0.20-0.40

S55C steel Mechanical Propertities

Grade Condition Yield Strength

(Mpa)
Tensile Strength
Rm
(Mpa)
Elon-
gation
A5
(%)
Hardness
HRC
Quenching
Temperature
(℃)
Benda-
bility
Nominal Thickness,t
1.95mm≤t≤10.0mm
Rolled Annealed
  S55C Rolled
Annealed
Water-quenched
Oil quenched
500
350
825
550
2510
2120
18
30
61
57
805
845
Min.reco-mmended
Bending radius
(≤90°)
3.0
×t
1.0×t

BEBON steel can supply S35C,S40C,S45C,S50C,if you are interested in our products ,please contact us.


Bebon International is a professional S55C steel exporter and a steel Stockist in china. We keep more than 1000 tons S55C steel in stock every month. If you want to get the S55C steel price, please do not hesitate to contact us. Any need in S55C Chemical Composition and Mechanical Properties, please feel free to contact us by email or calling to us.
Share
Are you also interested in further steel processing (machining)?

Just like you, 70% customers choose long-term cooperation with BBN steel not only for our good product and service quality, good reputation in the international market, but also for our experienced one-stop raw material supply and further steel processing!

Fabrication and Machining Service24h Technical support

Spot Resource